PRODUCT DESCRIPTION

This two-component product is mainly prepared by aliphatic acrylic polyurethane resin, and anti-rust pigments. This product features:

● Good gloss and color retention

● Strong adhesion

● Fast drying

● Long durability

● Great resistance to salt & chemical corrosion, rust, impact

● Cures at temperatures down to -5 oC

● Etc

Typical Uses:

This product is typical used as finish paint for steel substrate as：

● Steel structure

● Ships

● Bridges

● Vehicle, machinery equipment

● Power plant

● Pulp mill and paper mills

● Traffic sign

● Chemical and petrochemical factory

这里可以自定义设置

PRODUCT SELLING POINT

● Nanotechnology, compact structure.

● Salt spray corrosion resistance ≥3000h,Resistance to aging≥5000h.

● 98% concentrated sulfuric acid for 1200h.

● Resistance to 30% hydrochloric acid for 1200h.

●Factory direct sale.

PRODUCT ADVANTAGES

Repair rate 0%, no downtime cost. Acceptance of all.

这里可以自定义设置

PRODUCT APPLICATION GUIDE

Mixing	Mix part A and part B as 20:4 by weight. Slowly add part B into part A and ensure mixed completely.
Thinner	BS52-10 exclusive thinner ≤ 10 % w./w.
Cleaner	BS52-10 exclusive thinner
Application methods	Airless spray (recommended)：Nozzle tip: 0.017-0.023 inch, minimum 150 bar/2100 psi. Brush: recommended. Roller: recommended.

MORE SPECIFIC COLORS PLEASE CONSULT US

DRYING SCHEDULE

	Product	Thickness
Primer	Epoxy zinc rich primer	50μm
Midcoat	Epoxy mica iron oxide paint	150μm
Topcoat	Acrylic polyurethane finish paint	2*40μm

*Color Variation:

Color may vary from batch to batch. JIANBANG ensures color variation ∆E≤0.2. Suggest use the same batch to achieve best color consistency

PRODUCT SPECIFICATIONS

Color	Custom color (aluminum light)
Gloss	High gloss
Density	~1.4kg/l
Hardness	Polyurethane curing agent
Solid Volume	≥ 50 %
Standard Film thickness	60um dry film thickness (about 120um wet film thickness)
Theoretical spreading rate	9.6-11.6@ 50~75 µm dry film